Quantitative phase analysis and thickness measurement of surface-oxide layers in metal and alloy powders by the chemical-granular method
1998
The principles of the chemical-granular analysis of metal and alloy powders are reviewed and the results are compared with those provided by the spectroscopic analytical techniques XPS, AES and SIMS, including ion etching in their depth-profiling mode, when they are applied to the same materials. Several examples are analysed and it is shown that the chemical-granular method alone can provide the very same information as depth profiling. However, it is averaged over a macroscopic powder sample in contrast to one or a few single particles. Nevertheless, it is the combination of the chemical-granular and depth-profiling analyses that really provides an unparalleled description in quantitative…
Physical chemistry of the powder metallurgy of beryllium: Chemical characterization of the powder in relation to its granularity
1996
Combining the systematic quantitative chemical analysis of the light impurities H, C, N, and O, the quantitative thermal desorption of molecular H2O and H2, and X ray diffractometry of various size fractions of a commercial Be powder (SP-65 grade from Brush-Wellman) allowed the precise de-termination of the mean composition and equivalent mean thickness of the surface impurity phases in the passivation-contamination layer on the surface of the particles. The overall surface stoichi-ometry is as follows: 0.2 BeOcrystallized, 0.8 [BeO - 0.59 H2O]amorphous, 0.14 H2Oads The result of the elemental analysis by X-ray photoelectron spectroscopy of the unetched surface of a powder pellet is compare…
Synthesis of Fullerene- and Nanotube-Like SnS2 Nanoparticles and Sn/S/Carbon Nanocomposites
2009
SnS2 nested fullerene-type (IF) nanoparticles, nanotubes, and SnS2/C hybrid nanostructures were obtained by vapor transport starting from elemental tin and CS2. The reaction was carried out in a single-step process by heating elemental tin metal powder in a horizontal tube furnace at 800−1000 °C. TEM analysis allowed proposing a plausible mechanism for the formation of fullerene-like particles of SnS2 as well as tubes and scrolls from nanosheets of SnS2. Pure material could be obtained by optimizing the reaction based on a product analysis using powder X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) combined with energy-dispersive X-ray spectroscopy (EDX…
Friction stir consolidation of aluminum machining chips
2017
Friction stir consolidation (FSC) is a solid-phase manufacturing process that consolidates metal powder, chips, or scraps into solid blocks via severe plastic deformation and solid state welding. It has the potential to be a more economical and âgreenâ process to recycle metal waste. In this study, solid discs were made from AA6061 aluminum alloy machining chips by FSC. The progression of the process was revealed by analyzing the motion of the tool, consolidating force, power history, and macro/microstructure of discs produced from a series of partial consolidation experiments. A bowl-shaped recrystallized zone in the vertical cross-sections of the disc products was observed and conside…
Spark plasma synthesis from mechanically activated powders: a versatile route for producing dense nanostructured iron aluminides
2004
Abstract The possibility of mechanically activated spark plasma sintering (MASPS) to perform simultaneously within a very short period of time the synthesis and the consolidation of nanophase iron aluminide from mechanically activated powders of Fe and Al in two different ratio (Fe53 at.% and Fe60 at.%) were confirmed in this work.